@InProceedings{LoiolaSaOsBaGaGo:2017:InCoMo,
author = "Loiola, P. T. C. and Sanches, R. M. and Oshiro, R. H. and Baldan,
Maur{\'{\i}}cio Ribeiro and Gama, A. M. and Gon{\c{c}}alves,
Emerson Sarmento",
affiliation = "{Instituto Tecnol{\'o}gico de Aeron{\'a}utica (ITA)} and
{Instituto de Aeron{\'a}utica e Espa{\c{c}}o (IAE)} and
{Instituto de Aeron{\'a}utica e Espa{\c{c}}o (IAE)} and
{Instituto Nacional de Pesquisas Espaciais (INPE)} and {Instituto
de Aeron{\'a}utica e Espa{\c{c}}o (IAE)} and {Instituto
Tecnol{\'o}gico de Aeron{\'a}utica (ITA)}",
title = "Polianilina eletrossintetizada em fibra de carbono:
influ{\^e}ncia da concentra{\c{c}}{\~a}o de mon{\^o}meros no
processo de cresicmento",
booktitle = "Anais...",
year = "2017",
pages = "303--306",
organization = "Congresso Brasileiro de Carbono, 7.",
keywords = "Polianilina, Fibra de Carbono, Eletross{\'{\i}}ntese,
Polyaniline, Carbon Fiber, Electrosynthesis.",
abstract = "A influ{\^e}ncia da concentra{\c{c}}{\~a}o de mon{\^o}meros de
anilina na eletross{\'{\i}}ntese de polianilina em fibras de
carbono aeron{\'a}utico foi o objeto de estudo deste trabalho. A
eletross{\'{\i}}ntese foi realizada em cabos de fibra de carbono
de 4 cm de comprimento, a uma taxa de varredura de 50 mV. s -1 ,
varrendo o potencial el{\'e}trico aplicado entre -0,5 V a 1,05 V
vs Ag/AgCl, por 9 ciclos. As concentra{\c{c}}{\~o}es de
mon{\^o}meros exploradas foram de 0,2 mol. L -1 e 0,5 mol. L -1 .
Observa-se que em baixa concentra{\c{c}}{\~a}o, 0,2 mol. L -1 ,
a forma{\c{c}}{\~a}o de polianilina {\'e} pequena, quase
impercept{\'{\i}}vel quando comparada a eletross{\'{\i}}ntese
realizada a 0,5 mol. L -1 .Em alta concentra{\c{c}}{\~a}o, a
fibra {\'e} recoberta por uma camada do pol{\'{\i}}mero,
resultando, entretanto, na forma{\c{c}}{\~a}o de
pol{\'{\i}}mero sobre pol{\'{\i}}mero (PANi sobre PANi),
perdendo especificidade entre os estados de oxida{\c{c}}{\~a}o
da polianilina. ABSTRACT: The influence of the concentration of
aniline monomers on polyaniline electrosynthesis in aeronautical
carbon fibers was the object of study of this work. The
electrosynthesis was performed on 4 cm long carbon fiber cables at
a scanning rate of 50 mV.s-1, sweeping the electric potential
applied between -0.5 V to 1.05 V vs Ag / AgCl, for 9 cycles. The
concentrations of monomers harvested were 0.2 mol.L-1 and 0.5
mol.L-1. It is observed that at low concentration, 0.2 mol.L-1,
the formation of polyaniline is small, almost imperceptible when
compared to electrosynthesis performed at 0.5 mol.L-1. In high
concentration, the fiber is covered by a layer of the polymer,
resulting, however, in the formation of polymer on polymer (PANi
on PANi), losing specificity among the oxidation states of
polyaniline.",
conference-location = "Campos do Jord{\~a}o, SP",
conference-year = "24-27 out.",
language = "pt",
ibi = "8JMKD3MGP3W34P/3Q5RLN5",
url = "http://urlib.net/ibi/8JMKD3MGP3W34P/3Q5RLN5",
targetfile = "Loiola_polianilina.pdf",
urlaccessdate = "27 abr. 2024"
}